FeSiB Alloy Strip Transformer Core Material 1k101 and 1k104 0.025mm Thickness
Brand Name:OHMALLOY
Certification:ISO9001-2008
Model Number:1K107
Minimum Order Quantity:50kg
Delivery Time:7 days
Payment Terms:L/C, T/T,
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
Room 311, No.1211, Mudanjiang Road, Baoshan district, Shanghai
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
FeSiB Alloy Strip Transformer Core Material 1k101 and 1k104 0.025mm Thickness
Frequency transformer iron core(50－60Hz)
IF power transformer iron core (400Hz－15kHz)
Switch power transformer iron core ( below 10kHz)
Filter reactor, filtering and energy storage inductor,
Power factor correction inductor core( below 50kHz)
Saturable reactor,Pulse compressor iron core
l High Saturation magnetic induction - reduce transformer volume
l High magnetic permeability low coercive force- improve transformer efficiency
l Low loss(Equivalent 1/3 1/5 of silicon steel sheet)- reduce transformer temperature rise
l Low magnetizing current - reduce primary coil copper loss of transformer
l Good temperature stability - under 130℃ for long-term work
Typical Properties
Physical properties of FeSiB alloy
| Saturation magnetic induction (Bs) | 1.56T | Hardness (Hv) | 960 |
| Curie temperature (TC) | 410℃ | Density (d) | 7.18g/cm3 |
| Crystallizing temperature( Tx) | 550℃ | Resistivity(r) | 130mW-cm |
| Saturation magnetostriction coefficient (ls) | 27×10-6 | Continuous operating temperature range | -55－130℃ |
Magnetic properties of FeSiB alloy
| Product Type | Transverse magnetic annealing | No magnetic annealing | Longitudinal magnetic annealing |
| Maximum permeability | >2×104 | >20×104 | >25×104 |
| Saturation magnetic induction | 1.5 T | 1.5 T | 1.5 T |
| Residual magnetic induction | <0.5 T | 0.6-1.0 T | 1.2 T |
| Coercive force | <4A/m | <6 A/m | <2.5A/m |
| Loss(50Hz, 1.4T) | <0.2W/kg | <0.13W/kg | <0.25W/kg |
| Loss(400Hz, 1.2T) | <1.8W/kg | <1.25W/kg | <2W/kg |
| Loss(8kHz, 1.0T) | <80W/kg | <60W/kg | <100W/kg |
| Iron loss rate(-55°C –125C ) | <15% | <15% | <15% |
| Iron loss rate(120℃200 H) | <15% | <15% | <15% |
| Performance indicators | FeSiB alloy | Si- steel |
| Saturation magnetic induction(T) | 1.56 | 2.03 |
| Coercive force(A/m) | <4 | <30 |
| Maximum permeability(Gs/Os) | >25×104 | 4×104 |
| Iron loss(W/kg) | 50Hz, 1.3T <0.2 | 50Hz, 1.7T =1.2 |
| Exciting power (VA/kg) | 50Hz, 1.3T <0.5 | 50Hz, 1.7T <0.83 |
| Laminated coefficient | >0.80 | 0.95 |
| Magnetostriction(×10-6) | 27 | 15 |
| Resistivity(Wm-cm) | 130 | 45 |
| Density(g/cm3) | 7.18 | 7.65 |
| Tx(℃) | 550 | － |
| Curie temperature(℃) | 415 | 746 |
| Tensile strength(Mpa) | 1500 | 343 |
| Vickers hardness(HV) | 900 | 181 |
| Thickness(μm) | 30 | 300 |
Size:
| grade | width (mm) | thickness (mm) |
| 1K101 | 3.2～50 | 27～36 |
Other specifications of the strip can be offered according to customer requirements.