MV LV 10KV 35KV XLPE Compound Insulation Material For LT And HT Cables
Brand Name:Anan
Certification:Reach,Rohs
Model Number:XLPE
Minimum Order Quantity:1000 KGS
Delivery Time:1 week
Payment Terms:L/C, T/T
Contact Now
Add to Cart
Verified Supplier
Location:
Dongguan Guangdong China
Address:
Room NO.701.702.712. Building 3,Onemall First International,Nancheng District,Dongguan,Guangdong,China.
Supplier`s last login times:
within 37 hours
Product Details
Company Profile
Product Details
MV LV 10KV 35KV XLPE Compound Insulation Material for LT and HT Cables
Product Description:
XLPE is another material which is used as insulation material.
XLPE can be used across low voltage cables up to high voltage cables as it possesses enhanced properties as compared to other insulating materials like PVC.
It offers high tensile strength, impact resistance, insulation and won’t melt at elevated temperatures.
XLPE insulation provides a high water tree resistance due to which this particular insulation is suitable for LT and HT cables.
Cross linked polyethylene for low Voltage Cable XLPE-LV
Jiangxi Anan offers different products with best processing and testing and ambient curing properties. our XLPE is a saline cross linkable natural compound designed for low voltage power cables. The base material in combination with the catalyst Masterbatch will accelerate the moisture included crosslinking reaction. The system is highly active and crosslinks quickly in sauna or hot water. the product range covers the power and overhead applications.
Product Show
Application
Specification :
Peroxide cross-linked polyethylene XLPE
| Products | Application |
| XLPE compound up to 10KV | Insulation for XLPE cable up to 10KV |
| XLPE compound up to 35KV | Insulation for XLPE cable up to 35KV |
Technical Data Sheet
Items | Unit | Up to 10KV | Up to 35KV | ||
| Standard Value | Typical Value | Standard Value | Typical Value | ||
| Density | g/cm3 | 0.92±0.02 | 0.913 | 0.92±0.02 | 0.915 |
| Tensile Strength | MPa | ≥17 | 18.3 | ≥17 | 19.5 |
| Break Elongation | % | ≥500 | 598 | ≥500 | 605 |
| Hot set test Elongation under load(200°C0.2MPa15min) | % | ≤80 | 55 | ≤80 | 58 |
| Hot set test Permanent Deformation(200°C0.2MPa15min) | % | ≤5 | 3 | ≤5 | 2 |
| Variation of Tensile Strength after Ageing | % | ±20% | 7 | ±20% | 11 |
| Variation of Break Elongation after Ageing | % | -9 | -14 | ||
| gel content | % | ≥80 | 84 | ≥80 | 86 |
| Low temperature embrittlement(-76°C) | Piece | ≤15/30 | 0/30 | ≤15/30 | 0/30 |
| Dielectric constant(20°C50Hz) | / | ≤2.35 | 2.25 | ≤2.35 | 2.15 |
| Volume Resistance @ 20°C | Ω.m | ≥1*10^14 | 1*10^15 | ≥1*10^14 | 6*10^14 |
| Dielectric strength @ 20°C | MV/mm | ≥30 | 40 | ≥30 | 42 |
Production Package
How To order :
1. Let me know the models, specification, quantities, colors you
want to order
2. We will email you the Proforma Invoice based on your order
information
3. Kindly check the PI, everything is ok, we will start production
as soon as receiving payment deposit or LC, then deliver the goods
on request, original documents will be send against full payment
Welcome to Inquiry!
MV LV 10KV 35KV XLPE Compound Insulation Material For LT And HT Cables