Silane Crosslinkable Xlpe Cable Compound / Polyethylene Compound Linear Type
Brand Name:Herrman
Certification:ISO9001:2015,CE,ROSH,SGS
Model Number:/
Minimum Order Quantity:1000 KGS
Delivery Time:45 working days
Payment Terms:L/C, T/T, D/A, D/P，By Negotiation
Contact Now
Add to Cart
Site Member
Location:
Hefei Anhui China
Address:
16th Floor, Building C, Fortune Plaza, No.287, Suixi Road, Hefei, Anhui, China
Supplier`s last login times:
within 27 hours
Product Details
Company Profile
Product Details
Silane crosslinkable in Room Temperature Polyethylene Insulation Compound and Catalyst Polyethylene Insulation Compound
Description
Silane crosslinkable in Room Temperature Polyethylene Insulation Compound and Catalyst are used as cable cross linkage material.
Feature
1 Appearance: White
2 Component content: polyethylene 97%, silane 1 ~ 2%, antioxidant 0.1 ~ 0.5%, other 0.5 ~ 1%
3 Type and proportion of monomer unit: ethylene, 97%
4 Linear type
5 Specific gravity: 0.925 g/cm3
Main Specification
| NO. | Testing Item | Unit | Index | Value |
| 1 | Tensile Strength | MPa | ≥13.5 | 23.5 |
| 2 | Elongation at break | % | ≥350 | 730 |
| 3 | Impact brittle temperature | |||
Test Temperature | ℃ | －76 | -76 | |
Impact embrittlement performance | ≤15/30 | -0/+30 | ||
| 4 | 135±2℃×168h] Air heat ageing | |||
Rate of change of tensile strength | % | ±20 | +7 | |
Rate of change of elongation at break | % | ±20 | -6 | |
| 5 | (200℃,0.2 Mpa,15min) Hot prolongation | |||
Elongation under load | % | ≤100 | 95 | |
Permanent deformation after cooling | % | ≤5 | 5 | |
| 6 | Gel content | % | ≥60 | 69 |
| 7 | Dielectric loss angle tangent | ≤1.0×10-3 | 7.1×10-4 | |
| 8 | Dielectric constant | ≤2.35 | 2.32 | |
| 9 | 20℃ volume resistivity | Ω.m | ≥1×1014 | 4.4×1014 |
| 10 | Dielectric strength | MV/m | ≥25 | 30 |
Product Photo
Silane Crosslinkable Xlpe Cable Compound / Polyethylene Compound Linear Type
Inquiry Cart
0