Good Stability High Anticorrosive Performance Electrophoretic Paint For Kitchen Guards
Brand Name:HAOLISEN
Certification:IATF16949 , ISO9001
Model Number:HS-6060LB/HS-2568G
Minimum Order Quantity:Negotiation
Delivery Time:30-60 Days
Place of Origin:Shanghai China （Mainland）
Contact Now
Add to Cart
Verified Supplier
Location:
Shanghai Shanghai China
Address:
15/F, No.1185, Huyi Road, Jiading District, Shanghai，China.
Supplier`s last login times:
within 1 hours
Product Details
Company Profile
Product Details
High performance electrophoresis paint for kitchen guards
Product Introduction :
HS-6060LB/HS-2568G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. |
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc. |
Main ingredients :
Additives: surface active agent, prevent shrinkage cavity agent | |
Solvent: alcohol ether | Neutralizing agent: organic acid |
Matrix resin: Acrylic modified epoxy resin | |
Product quality data :
| Project | Technical data | Test standard | ||
| Resin (HS-6060LB) | Gray Paste(HS-2568G) | |||
| Appearance | —— | Milky white liquid | Gray viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 1000.00-1250.00
Paste 250.00
DI water 1900.00-2200.00
Total 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000～4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of parts coated)
Storage, packaging and transportation :
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.