ISO9001 Corrosion Protection Combined Zinc Flake Coating

Dip Spin Zinc Flake Coating With Microlayer Corrosion Protection

1 Zinc Flake Coating Information

Trade Name: Zincover

Article/Model No.:JH-9382

2 Composition/information on ingredients

JH-9382 is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.

Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

3 Coating Process

3.1 Mix Ratio

Pack A:16.0 kg

Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)

Pack C:0-50 g (according to different viscosity demand )

3.2

3.3

3.4

Stir the mixture about 1~2 hours fast after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours continuously.

3.5

The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

v

3.6

Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

3.7

Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.

5 Technical data

6 Mix Diagram

Caution: Temperature should be controlled in above operation.

7 Packing

(For special packaging)

10 Quality guarantee period

Before compound 6 months at 20℃

After compound 30 days at 20℃ ( It can be recycled if adding fresh coating continuously. )

It should be stored under 20℃ if not in use.

Changzhou Junhe Technology Stock Co., Ltd. is a high-tech enterprise devoted to developing industrial fine chemicals, special equipment and services solution provider which was founded in Changzhou, Jiangsu in 1998.

Zinc flake microlayer corrosion protection coating is one of our core products, our company draw on the experience and lesson of dacromet coating technology from Japan and USA, investing millions on R&D, after 20 years application and diffusion, Junhe zinc flake microlayer corrosion protection coating already become one of the leading brand in China.

Our company have three industrial base: chemical production base, equipment production base, coating job processing base.

Equipment Production Base

Chemical Production Base

Coating Job Processing Base

Company research and development center is located in changzhou national hi-tech zone, owns 15 acres of land for construction and is built around five categories of chemicals and equipment research and development and incubation bases, equipped with standardization on the basis of the experimental equipment and testing equipment of the company's marketing center and two functional departments in the changzhou new north area to create building, the company's three big center and subsidiary system solution for customer demand to provide a solid foundation. The company has passed ISO9001 and TS16949 system certification.

Our Qualification