Water Solution Zinc Phosphate Coating Paint And Chrome Free Spraying Fot Hardware

Water Solution Zinc Phosphate Coating / Zinc Aluminium Flake Coating

Zinc Phosphate CoatingTechnical data

6 Mix Diagram

Caution: Temperature should be controlled in above operation.

2 Coating Process

2.1 Degreasing

The workpiece should be degreased if there is oil on the surface. There are three processing methods:

1.High temperature

2.Neutral water-base degreasing agent

3.Organic solvent such as methylene chloride.

2.2 Derusting

The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.

2.3 Coating

The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.

2.4 Pre-heating

The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)

2.5 Curing

The workpiece after pre-heating should be cured at 310-340℃ for 20-40mins. ( according to heat absorption of workpiece.)

3 Attentions

Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

4 Packing

(For special packaging)

10 Quality guarantee period

Before compound 6 months at 20℃

After compound 30 days at 20℃ ( It can be recycled if adding fresh coating continuously. )

It should be stored under 15℃ if not in use.

Changzhou Junhe Technology Stock Co., Ltd. is a high-tech enterprise devoted to developing industrial fine chemicals, special equipment and services solution provider which was founded in Changzhou, Jiangsu in 1998.

Zinc flake microlayer corrosion protection coating is one of our core products, our company draw on the experience and lesson of dacromet coating technology from Japan and USA, investing millions on R&D, after 20 years application and diffusion, Junhe zinc flake microlayer corrosion protection coating already become one of the leading brand in China.

Our company have three industrial base: chemical production base, equipment production base, coating job processing base.

Equipment Production Base

Chemical Production Base

Coating Job Processing Base

Company research and development center is located in changzhou national hi-tech zone, owns 15 acres of land for construction and is built around five categories of chemicals and equipment research and development and incubation bases, equipped with standardization on the basis of the experimental equipment and testing equipment of the company's marketing center and two functional departments in the changzhou new north area to create building, the company's three big center and subsidiary system solution for customer demand to provide a solid foundation. The company has passed ISO9001 and TS16949 system certification.

Our Qualification