Long-Lasting Solution Black and Green HDPE Smooth Geomembrane s Excellent Aging and UV Resistance
Brand Name:JianYi
Certification:ISO9001
Place of Origin:China
Puncture Resistance:240-960N
Chemical Resistance:Excellent
Tear Strength:93-374N
Contact Now
Add to Cart
Verified Supplier
Location:
Changsha Ningxia China
Address:
Chuangye Avenue,Ningxiang Economic Development Zone,Changsha City,Hunan Province,P.R.C.
Supplier`s last login times:
within 19 hours
Product Details
Company Profile
Product Details
Long-Lasting Solution Black and Green HDPE Smooth Geomembrane s Excellent Aging and UV Resistance
Product Introduction
The black and green double-color HDPE geomembrane is a type of geomembrane made from high-density polyethylene (HDPE) or low-density polyethylene (LLDPE) raw materials with two different color masterbatches added, which are then co-extruded and blown into a geomembrane. Typically, one side of this geomembrane is black, and the other side is green, hence the name black and green double-color HDPE geomembrane.
Product Properties
Chemical stability
The black and green dual-color HDPE geomembrane has excellent chemical stability, capable of resisting the corrosion of more than 80 kinds of strong acid and alkali chemical media. It is suitable for environments such as sewage treatment, chemical reaction pools, and waste landfills.
Text: Resistance to aging
This geotechnical membrane has excellent resistance to aging, ultraviolet radiation, and decomposition, allowing for long-term use in open environments. The material's lifespan can reach 50-70 years, providing a reliable material guarantee for environmental impermeability.
Resistant to plant roots
The black and green dual-color HDPE geomembrane has excellent puncture resistance, capable of withstanding the invasion of most plant root systems.
High mechanical strength
It has good mechanical strength, with a breaking tensile strength of 28 MPa and a high breaking elongation rate of up to 700%, capable of withstanding significant physical stress.
Cost-effectiveness
Although new technologies have been adopted to improve the impermeability effect, its production process is more scientific and faster, resulting in a product cost that is actually lower than traditional waterproof materials. Generally, using HDPE impervious membrane in engineering can save about 50% of costs.
Easy construction
This geomembrane has high flexibility, with various specifications and laying forms to meet the impermeability requirements of different projects. It adopts hot-melt welding technology, which provides high seam strength, convenient and fast construction.
Environmentally friendly and non-toxic
The black and green dual-color HDPE geomembrane is made of non-toxic and environmentally friendly materials. Its impermeable principle is based on ordinary physical changes and does not produce any harmful substances. It is an ideal choice for environmental protection, aquaculture, and drinking water pools.
Product Application
The black and green dual-color HDPE geomembrane is mainly used for covering the surface of landfills in the middle stage, covering slopes, and covering waste disposal sites. During the laying process, the green side faces up and the black side faces down. The green side is required to have anti-aging, antioxidant, and light stabilizer properties to ensure that the product can be used for more than five years under direct sunlight conditions. The black side mainly plays a role in preventing rainwater from infiltrating into the landfill, thereby increasing the service life and reducing the cost of leachate treatment.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | |||||||||
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Density (g/c㎡,≥) | 0.939 | ||||||||
| Tensile Properties | |||||||||
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yeild Elongation Rate (%) | 12 | ||||||||
| Breaking Elongation Rate (%) | 700 | ||||||||
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) | 300 | ||||||||
| Carbon Black | |||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | ||||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | ||||||||
| Oxidative Induction Time (OIT) | |||||||||
| Standard OIT (min) | 100 | ||||||||
| High Pressure OIT (min) | 400 | ||||||||
| 85℃ Oven Ageing (Minimum Average) | |||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | ||||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | ||||||||
| The Anti-UV Strength | |||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | ||||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | ||||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | ||||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | ||||||||
| Dimensional Stability | ±2 | ||||||||
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
| Specification Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark | |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | ||
| Density (g/c㎡,≥) | 0.94 | ||||||||||
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | ||
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | ||
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |||||||
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | ||||||||||
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | ||
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | ||
| Carbon Black Content (%) | 2.0~3.0 | ||||||||||
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not allowed | ||||||||||
Long-Lasting Solution Black and Green HDPE Smooth Geomembrane s Excellent Aging and UV Resistance