2000T/M Aluminum Profile Anodizing Production Line For Window

2000T/M Aluminum profile Anodizing Production Line for window

一. Product description:

1.Anodizing facilities are deploying intelligent workflow management platforms that automate the coordination of various production, quality, and maintenance processes, optimizing resource allocation, streamlining decision-making, and enhancing overall operational efficiency.

2.Anodizing production lines are integrating additive manufacturing capabilities to produce custom-designed spare parts and components on-demand, reducing inventory costs, lead times, and the risk of production downtime due to part unavailability.

3.Anodizing production lines are employing adaptive control systems that continuously monitor and adjust process parameters in real-time, based on feedback from in-line sensors and advanced analytics, to maintain optimal coating quality and consistency, even in the face of changing environmental conditions or material variations.

二. Design Condition:

四. Treatment Process:

1. Degreasing
   (1) 6jig(rack)/ tank x 1 tank=6jig(rack)
   (2) treatment time: 2-5min
2. Alkaline Etching
   (1) 6jig(rack) / tank x 2 tank=12jig(rack)
   (2) treatment time: 3-15min
3. Neutralization
   (1) 6jig(rack) / tank x 1 tank=6jig(rack)
   (2) treatment time: 1-5min
4. Anodizing
   (1) 3 jig(rack)/tank x 6tanks = 18jig(rack)
   (2) Current density: 130A/m²
   (3) Process time: 30min
   (4) Unprocess time: 10min
   (5) Total time 30+10=40min

(6) Average anodizing layer : 0.36*1.3*30*0.77 =10.81um

5. Colour 1

1) Clour process: Mix Salts

2) Quantity:3 jig(rack)/tank x 1tanks = 3jig(rack)

3) Current density: 70A

4) Process time: 2-8min

6. Sealing
1) Sealing menthod: Sealing at Medium or Normal Temperature
2) Quantity: 6jig(rack)/tank x 1 tank
3) Process time 10-15min

五.Process Tank

1. Degreasing 【Free sulfuric acid 180±30 g/l】 1 Tank
2. Alkaline Etching【Free alkali 40-60g/l,Al3+ 30-120g/】 2 Tanks
3. Neutralization 【Free sulfuric acid180±20g/l】 1 Tank
4. Anodising 【Free sulfuric acid 140-180g/l,Al3+≤20g/l】 6 Tanks
5. Colouring 【stannous sulfate 3-8g/l,Free sulfuric acid 15-25g/l,PH 0.8-1.2】 3 Tanks
6. Medium Temperature Sealing【PH 5-6.5,Nickel ion0.8-1.3g/l,Fluorion0.3-0.7 g/l】 3 Tank

六. Design Parameter and Setting

1. Anodizing treatment area:
1) Each anodizing process tank need 40min ,where total jig(rack)/year:​

( 3 rack x 6 tank x 60min/h) ÷40min x600 hour =16200jig(rack)

2) Design 50m²^/jig(rack) . Where every tank is 100m²
3) Area treatment/year : 16200jig(rack)x 50m² /jig =810000m²

2. Anodizing treatment weight:
Monthly output : 810000m²÷350m²/T*0.9=2082T≧2000T

3. Power consumption:
1) Anodising Tank:100m²/tank* 130A/ m²÷0.9=14444A/tank

Power Rectifier : 15000A =6unit
2) Clouring tank: 100㎡/tank×70A/m²÷0.9 = 7777A/tank

Colour Rectifier : 8000A =3 unit

七. Process Chat

MEI-AL Technology has been committed to serve the aluminum profile surface treatment industry with its strong technical force, excellent production and processing, scientific management methods and excellent management style. Mei-al main production: anodizing, coloring, electrophoresis production line, products have special high-power silicon control rectifier, high-power high-frequency switching power equipment, electrophoresis workshop pure water equipment(RO machines), refining equipment, electrophoretic paint recovery equipment, electrophoresis curing furnace,loading and unloading machines,1T+1T professional anodizing cranes, anodizing tank temperature control system and production line automatic control system, etc.

In our perpetual effort and support of our partners in the industry,MEI-AL Technology has obtained outstanding achievements and is still maintaining a rapid development speed.With the operation spirit of “Professional, Concebtration, Integrity, Co-win”, MEI-AL Technology will provide with you excellent products and perfect services, in the rooted concept of Growind Up with You !