Invar 36 Invar Alloy Pernifer 36 ASTM F1684 Iron Nickel Alloy Antenna Components Light Rod
Brand Name:KAIXIN
Certification:ISO9001:2015
Model Number:KX-Alloy INVAR 36
Minimum Order Quantity:200KG
Delivery Time:45~60days
Payment Terms:T/T, L/C
Contact Now
Add to Cart
Verified Supplier
Address:
The North East of Danlv Bridge, Aerospace Industry Park, Lvcheng Town,Danyang City,Jiangsu Province
Supplier`s last login times:
within 48 hours
Product Details
Company Profile
Product Details
KX Invar 36 Solid Solution Iron Nickel Alloy Antenna Components Light Rod For Invar Alloy
Product Description and Application
Invar 36 is also known as Nilo 36,Pernifer 36, ASTM F1684, UNS K93600,
Invar 36 has low coefficient of expansion and good plasticity at -60 ° C to 80 ° C atmospheric temperature variations. It is a special iron nickel alloy with an ultra-low coefficient of expansion. The control of carbon and manganese components is very important. It has a stable low expansion coefficient in a specific temperature range. Invar36 is resistant to corrosion in dry air at room temperature. Corrosion (rust) will occur in other harsh environments, such as humid air.
Applications: bimetallic active layer materials, clamps for measuring instruments, astrotelescope components, optical instruments, metal molds for CFRP, antenna components, shielding frames for FPD, inspection clamps for semiconductor, processing clamps for semiconductor, temperature controller and waveguide.
Process Performance and Requirements
- Product Fusion Process
Vacuum Induction Furnace(VIM) and Electroslag Remelting Furnace(ESR)
- Product Chemical Composition
| Alloy Grade | Chemical Composition(Mass Fraction) % | |||||||||
C | P | S | S | Se | Cu | Mn | Ni | Co | Fe | |
Not more than | ||||||||||
Invar 36 | 0.05 | 0.02 | 0.02 | 0.3 | -- | -- | 0.20~0.60 | 35.0~37.0 | -- | Rem |
- Product Physical Property
Density | 8.1g/cm3 |
Fusing Temperature | 1430℃ |
| Alloy Grade | Sample Heat Treatment Institution | Average Coefficient of Linear Expansion,1/℃ | |
20℃~100℃ | 20℃~100℃ | ||
| Invar 36 | The semi-finished sample was heated to 840 ° C ±10 ° C, held for 1 hour, then water quenched. The sample was processed into finished sample, held for 1 hour at 315 ° C ±10 ° C, and cooled with the furnace or air | ≤1.5 | --- |
- Productive Process
Professional Customization
| Cold-drawn Wire | ¢0.3~¢18mm(Delivery in rolls or trays) |
| Hot-Rolling Wire | ¢5.5~¢20mm(Delivery in rolls) |
| Strip | thickness 0.1~4.5*width 6~350mm(Supply in rolls or straight strips) |
| Smooth Forged Rod on a Lathe | ¢60~350mm,L800-2500mm |
| Hot-rolled Burnishing | ¢20~80mm,L1000-5000mm |
| Cold Drawn and Burnishing | ¢2.5~18mm,L1000-8000mm |
| Seamless Tube | ¢1~275mm,wall thickness 0.2~30,L1000-8000mm |
Invar 36 Invar Alloy Pernifer 36 ASTM F1684 Iron Nickel Alloy Antenna Components Light Rod