0.01mm~200mm Metal Brass Sheet Polished Surface For Decoration 1/2H CuZn40 CuZn37
Brand Name:Modern
Certification:SGS
Model Number:CuZn40 CuZn37
Minimum Order Quantity:100kg per size
Delivery Time:5-7 working days, prompt delivery
Payment Terms:T/T, Western Union, MoneyGram
Contact Now
Add to Cart
Active Member
Location:
Liaocheng Shandong China
Address:
Wealth Center,Economic Development Zone,Liaocheng City,Shandong Province,Zip Code 252000,China.
Supplier`s last login times:
within 37 hours
Product Details
Company Profile
Product Details
Stock Polished 1/2H CuZn40 CuZn37 brass sheet for decoration
Product Description
| 1． | Item | Stock Polished 1/2H CuZn40 CuZn37 brass sheet for decoration | |
| 2． | Standard | ASTM,AISI,EN,BS,JIS,ISO,GB | |
| 3． | Material | C10100,C10200,C10300,C10400,C10500,C10700,C10800,C10910, C10920,C10930,C11000,C11300,C11400,C11500,C11600,C12000, C12200,C12300,TU1,TU2,C12500,C14200,C14420,C14500, C14510,C14520,C14530,C17200,C19200,C21000,C23000,C26000, C27000,C27400,C28000,C33000,C33200,C37000,C44300,C44400, C44500,C60800,C63020,C65500,C68700,C70400,C70600,C70620, C71000,C71500,C71520,C71640,C72200,etc. | |
| 4． | Specifications | Thickness | 0.1mm~200mm |
| Width | 6mm~2500mm | ||
| 5. | Length | 10mm~12000mm, or as required. | |
Brass is an alloy of copper and zinc. The simplest brass is a
copper-zinc binary alloy, called simple brass or ordinary brass.
Changing the zinc content in brass can obtain brass with different
mechanical properties. The higher the zinc content in brass, the
higher the strength and the lower the plasticity. The zinc content
of brass does not exceed 45%, and the higher the zinc content will
produce brittleness, which will deteriorate the alloy performance.
In order to improve the performance of brass, brass with other alloying elements is called special brass. Commonly used alloying elements are silicon, aluminum, tin, lead, manganese, iron and nickel. Adding aluminum to brass can increase the yield strength and corrosion resistance of brass, and slightly reduce plasticity. Brass containing less than 4% aluminum has good comprehensive properties such as processing and casting. Adding 1% tin to brass can significantly improve the resistance of brass to seawater and marine atmospheric corrosion, so it is called "Navy Brass". Tin also improves the machinability of brass. The main purpose of adding lead to brass is to improve machinability and wear resistance. Lead has little effect on the strength of brass. Manganese brass has good mechanical properties, thermal stability and corrosion resistance; adding aluminum to manganese brass can also improve its performance and obtain a smooth surface casting. Brass can be divided into two types of products: casting and pressure processing.
In order to improve the performance of brass, brass with other alloying elements is called special brass. Commonly used alloying elements are silicon, aluminum, tin, lead, manganese, iron and nickel. Adding aluminum to brass can increase the yield strength and corrosion resistance of brass, and slightly reduce plasticity. Brass containing less than 4% aluminum has good comprehensive properties such as processing and casting. Adding 1% tin to brass can significantly improve the resistance of brass to seawater and marine atmospheric corrosion, so it is called "Navy Brass". Tin also improves the machinability of brass. The main purpose of adding lead to brass is to improve machinability and wear resistance. Lead has little effect on the strength of brass. Manganese brass has good mechanical properties, thermal stability and corrosion resistance; adding aluminum to manganese brass can also improve its performance and obtain a smooth surface casting. Brass can be divided into two types of products: casting and pressure processing.
Datasheet for CuZn37
| Chemical Composition | ||||
| Element | ||||
| Cu(1) | Pb | Zn | Fe | |
| (1) Cu + Sum of Named Elements 99.7% min. | ||||
| Min (%) | 61.0 | |||
| Max (%) | 64.0 | 0.09 | Rem | 0.05 |
| Physical Properties | |
| Melting Point - Liquidus°F | 1680 |
| Densitylb/cu in. at 68°F | 0.305 |
| Specific Gravity | 8.44 |
| Electrical Conductivity% IACS at 68°F | 27.6 |
| Thermal Conductivity Btu/ sq ft/ ft hr/ °F at 68°F | 67 |
| Coefficient of Thermal Expansion 68-57210⁻⁶ per °F (68 – 572°F) | 11.4 |
| Specific Heat Capacity Btu/ lb /°F at 68°F | 0.09 |
| Modulus of Elasticity in Tension ksi | 15000 |
| Modulus of Rigidity ksi | 5600 |
Products' photos
FAQ
Q: Do you accept sample order?
A: Yes sure, please contact us for details.
Q: Are you a manufacturer or trading company?
A: We are a specialized manufacturer.
Q: How about the delivery terms?
A: 1. Payment: T/T, Western Union, Paypal, 30% deposit in advance and balance before delivery.
2. Min. Order Quantity: 100KG, or as required.
3. Transportation: By express (DHL,TNT,FedEx),air,sea,and train.
Q: How does your company control the quality?
A: Quality first. In order to guarantee high quality for our products,
Modern always makes a serious inspection for all products and raw materials in strict procedure.
Q: How about your after-sales service?
A: As a professional steel exporter, we offer promote technology support for all problems and questions.
Besides, we accept goods return or replace for quality problem.
0.01mm~200mm Metal Brass Sheet Polished Surface For Decoration 1/2H CuZn40 CuZn37
Inquiry Cart
0