Z8CND17-04 Turbine Blade Steel S165M Material
Brand Name:PANGANGGROUP,ANSTEEL,TISCO,BAOSTEEL
Certification:SGS,TUV,BV,ISO,MTC
Model Number:Z8CND17-04
Minimum Order Quantity:Negotiations
Delivery Time:Ex-stock for delivery: 5-7 days Production lead time: 35-45 days
Payment Terms:T/T
Contact Now
Add to Cart
Active Member
Location:
Mianyang China
Address:
Building 4A, Cross-border E-commerce Industrial Park, Shiqiaopu, High-tech Zone, Mianyang City, SC, China
Supplier`s last login times:
within 22 hours
Product Details
Company Profile
Product Details
Z8CND17-04 Turbine Blade Steel S165M Material
Description
Z8CND17-04 Turbine Blade Steel S165M Material is one of the better martensitic grades, showing sufficient corrosion resistance, good strength properties and high hardness with reduced carbon content. Z8CND17-04 Turbine Blade Steel S165M Material has very good strength and corrosion resistance of welded joints, resistance to fatigue, very good parameters in low temperature environments, and corrosion resistance comparable to austenitic steels 18-8.
Our company provides Z8CND17-04 Turbine Blade Steel S165M Material. All of Z8CND17-04 Turbine Blade Steel S165M Material conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Products Details
| Chemical Composition (weight%): |
| C (％): ≤ 0.05 |
| Si (％): ≤ 0.75 |
| Mn (％): - |
| P (％)≤: - |
| S (％)≤: - |
| Cr (％):≤ 16.0 |
| Ni (％): ≤ 5.00 |
| Mo (％): ≤ 1.00 |
| Cu (%): ≤0.03 |
| Mechanical Properties Under Final Heat Treatment: |
| Annealed condition +A for dimensions Min 16mm Tensile strength, Rm: <1100 MPa Hardness, HB: <320 for dimensions Min 16mm Tensile strength, Rm: <1150 MPa Hardness, HB: <380 Heat-treated condition +QT760 for bars Tensile strength, Rm: 760 - 960 MPa The yield point, Re: Min 550 MPa |
| Elongation, A:Min 16% Impact resistance for dimensions KV20℃: Min 70J Heat-treated condition +QT900 for bars Tensile strength, Rm: 900 - 1150 MPa The yield point, Re: Min 700 MPa |
| Elongation, A:Min 10% Impact resistance for dimensions KV20℃: Min 60J Heat-treated condition +QT840 for bars Tensile strength, Rm: 840 - 1100 MPa The yield point, Re: Min 660 MPa |
| Elongation, A:Min 14% Impact resistance for dimensions KV20℃: Min 55J Other mechanical and physical properties Modulus of elasticity, E = 200 GPa Thermal capacity, c-1 Thermal conductivity, λ = 15 W * m-1 Specific resistance, Ω: 0,8 mkOhm * m |
Applications:
Z8CND17-04 Turbine Blade Steel S165M Material used most often in the valves, turbine subassemblies, shafts, pins, pistons, crankshafts, agitators in the chemical, energy, marine, shipbuilding, etc.
Z8CND17-04 Turbine Blade Steel S165M Material
FAQ
Q: How do you control the quality?
A: We have professional inspectors to analyze the chemical composition of Z8CND17-04 Turbine Blade Steel S165M Material and test the finished products in strict accordance with the standards stipulated in the contract. In this process, the inner and outer surfaces, the appearance of both ends, bending, set length, outer diameter and Wall thickness will be checked one by one. You can rest assured that all products you receive from us are reliable.
Q: Do you accept customization?
A: Yes. If you have special requirements for products or packaging,
we can make them for you.
Q: Can you accept trial orders?
A: Our MOQ is usually 1 ton. However, if you want to place an order
as the start of our cooperation, we can accept smaller quantities
at the first time. Of course, after the start, we will have further
and longer cooperation.
Q: How do I get samples?
A: Free samples are available for your inspection and testing,
DHL/FedEx/UPS accounts can be used for sampling, and the courier
fee is borne by you.
Submit an enquiry for the displaying steel materials you are interested in TODAY!
Sales Engineer: sales@ss-bars.com
Z8CND17-04 Turbine Blade Steel S165M Material
Inquiry Cart
0